Effect of CPP-ACP on remineralization of artificial caries-like lesion: an in situ study

Abstract The purpose of this double-blind, randomized, crossover in situ study is to compare remineralization of preformed enamel lesions by casein phosphopeptide-stabilized amorphous calcium phosphate (CPP-ACP) and fluoride dentifrice products. During each of four 10-day experimental legs, 10 participants wore intraoral removable palatal acrylic appliances with four human enamel slabs with preformed lesions. A 0.03-mL treatment paste was dripped extraorally onto the enamel blocks once a day for 3 min. The four randomly allocated treatments were as follows: CO- Control: silica dentifrice without fluoride; MP: MI Paste; MPP: MI Paste Plus and FD: Fluoride dentifrice - 1100 ppm F as NaF). Knoop surface hardness (SH) test was performed in three stages (T0 - sound enamel, T1 - after preformed lesion, and T2 - after treatment) and the cross-sectional hardness (CSH) test was performed after treatment using a 50-gram Knoop load for 15 s. Knoop hardness number (KHN) was similar between treatments. %SHr was significantly higher in the MP, FD, and MPP when compared to CO group (Kruskal-Wallis and Mann-Whitney tests, p < 0.05). Harder enamel was found in MP (75 μm) and FD groups at 75 to 175 μm. Treatment with DF, MP, and MPP promoted an increase of 20.27%, 19.24%, and 14.71%, respectively, in Integral Hardness Change (ΔIHC) when compared to CO (p<0.05). Remineralizing agents (MP, MPP, and DF) were able to inhibit demineralization of human enamel subjected to high cariogenic challenge in situ. DF had the greatest preventive potential against the progression of carious lesions.

Effect of fluoride dentifrice and casein phosphopeptide-amorphous calcium phosphate cream with and without fluoride in preventing enamel demineralization in a pH cyclic study

Abstract Casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) complexes are anticariogenic and capable of remineralizing the early stages of enamel lesions. The use of fluoride prevents dental decay and the association of CPP-ACP with fluoride can increase remineralization. Objective: To evaluate the effect of CPP-ACP and CPP-ACPF creams associated with a fluoride dentifrice to prevent enamel demineralization in a pH cyclic model. Material and Methods: Previously selected by surface microhardness (SH) analysis, human enamel blocks (n = 56) were submitted to daily treatment with dentifrice in a pH-cycling model. The enamel blocks were divided into four groups; G1: Crest™ Cavity Protection - Procter & Gamble (1,100 ppmF of NaF); G2: Crest™ +MI Paste (MP) - Recaldent™ GC Corporation Tokyo, Japan); G3: Crest™ + MI Paste Plus (MPP) - Recaldent™ 900 ppm as NaF, GC Corporation Tokyo, Japan), and G4: control, saliva. Specimens were soaked alternatively in a demineralizing solution and in artificial saliva for 5 d. The fluoride dentifrice, with proportion of 1:3 (w/w), was applied three times for 60 s after the remineralization period. The undiluted MP and MPP creams were applied for 3 m/d. After cycling, SH was re-measured and cross section microhardness measurements were taken. Results: The SH values observed for the groups G3 (257±70), G1 (205±70), and G2 (208±84) differed from the G4 group (98±110) (one-way ANOVA and Tukey's post hoc test). There were no differences between the groups G1xG2, G2xG3, and G1xG3 for demineralization inhibition. The percentage of volume mineral showed that, when applied with fluoride dentifrice, MPP was the most effective in preventing enamel demineralization at 50 µ from the outer enamel surface (Kruskal-Wallis and Mann Whitney p<0.05). Conclusion: Fluoride dentifrice associated with CPP-ACPF inhibited subsurface enamel demineralization.

Influence of biofilm formation on the mechanical properties of enamel after treatment with CPP-ACP crème

Abstract: The study aimed to investigate the effects of bacterial biofilms on changes in the surface microhardness of enamel treated with casein phosphopeptide—amorphous calcium phosphate (CPP-ACP) with and without fluoride. Human enamel blocks with incipient caries-like lesions were divided into four groups of 13: G1: Saliva (Control); G2: fluoride dentifrice (Crest™, 1100 ppm as NaF); G3: CPP-ACP (MI Paste; Recaldent™); and G4: CPP-ACPF (MI Paste Plus; Recaldent™ 900 ppm as NaF). The specimens were soaked in demineralizing solution for 6 h and remineralized in artificial saliva for 18 h alternately for 10 days. The dentifrice was prepared with deionized water in a 1 : 3 ratio (w/w) or applied undiluted in the case of the CPP-ACP group. The surface microhardness (SMH) was evaluated at baseline, after artificial caries, after pH cycling and treatment with dentifrices, and after incubation in media with Streptococcus mutans for biofilm formation. The biofilms were exposed once a day to 2% sucrose and the biofilm viability was measured by MTT reduction. The percentage of change in surface microhardness (%SMHC) was calculated for each block. The data were analyzed by nonparametric test comparisons (α = 0.05). The %SMHC values observed in G2 were different from those of G1, G3, and G4 (p < 0.05). After biofilm formation, %SMHC was positive in G2 and G4 when compared to G1 and G3, but resistance to demineralization after biofilm formation was similar in all groups. In conclusion, the presence of biofilms did not influence the treatment outcomes of anticaries products.